合金钢结构图的化学分析成分
|
化学成分范围和限度，百分比 |
| 符合美国钢铁协会的数量 |
C |
锰 |
PMax。 |
SMax。 |
如果 |
倪 |
Cr |
莫 |
| 4130 |
0.28/0.33 |
0.40/0.60 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15/0.25 |
| 4137 |
0.35/0.40 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15/0.25 |
| 4140 |
0.38/0.43 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15/0.25 |
| 4142 |
0.40/0.45 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15/0.25 |
| 4145 |
0.43/0.48 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15/0.25 |
| 4147 |
0.45/0.50 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15/0.25 |
| 4150 |
0.48/0.53 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15/0.25 |
| 4161 |
0.56/0.64 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.70/0.90 |
0.25/0.35 |
| 4320 |
0.17/0.22 |
0.45/0.65 |
0.035 |
0.040 |
0.20/0.35 |
1.65/2.00 |
0.40/0.60 |
0.20/0.30 |
| 4340 |
0.38/0.43 |
0.60/0.80 |
0.035 |
0.040 |
0.20/0.35 |
1.65/2.00 |
0.70/0.90 |
0.20/0.30 |
| 4419 |
0.18/0.23 |
0.45/0.65 |
0.035 |
0.040 |
0.20/0.35 |
--- |
--- |
0.45/0.60 |
| 4615 |
0.13/0.18 |
0.45/0.65 |
0.035 |
0.040 |
0.20/0.35 |
1.65/2.00 |
--- |
0.20/0.30 |
| 4620 |
0.17/0.22 |
0.45/0.65 |
0.035 |
0.040 |
0.20/0.35 |
1.65/2.00 |
--- |
0.20/0.30 |
| 4621 |
0.18/0.23 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
1.65/2.00 |
--- |
0.20/0.30 |
| 4626 |
0.24/0.29 |
0.45/0.65 |
0.035 |
0.040 |
0.20/0.35 |
0.70/1.00 |
--- |
0.15/0.25 |
| 4718 |
0.16/0.21 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.90/1.20 |
0.35/0.55 |
0.30/0.40 |
| 4720 |
0.17/0.22 |
0.50/0.70 |
0.035 |
0.040 |
0.20/0.35 |
0.90/1.20 |
0.35/0.55 |
0.15/0.25 |
| 4815 |
0.13/0.18 |
0.40/0.60 |
0.035 |
0.040 |
0.20/0.35 |
3.25/3.75 |
--- |
0.20/0.30 |
| 4817 |
0.15/0.20 |
0.40/0.60 |
0.035 |
0.040 |
0.20/0.35 |
3.25/3.75 |
--- |
0.20/0.30 |
| 4820 |
0.18/0.23 |
0.50/0.70 |
0.035 |
0.040 |
0.20/0.35 |
3.25/3.75 |
--- |
0.20/0.30 |
| 5120 |
0.17/0.22 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.70/0.90 |
--- |
| 5130 |
0.28/0.33 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
--- |
| 5132 |
0.30/0.35 |
0.60/0.80 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.75/1.00 |
--- |
| 5135 |
0.33/0.38 |
0.60/0.80 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.05 |
--- |
| 5140 |
0.38/0.43 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.70/0.90 |
--- |
| 5145 |
0.43/0.48 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.70/0.90 |
--- |
| 5147 |
0.46/0.51 |
0.70/0.95 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.85/1.15 |
--- |
| 5150 |
0.48/0.53 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.70/0.90 |
--- |
| 5155 |
0.51/0.59 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.70/0.90 |
--- |
| 6150 |
0.48/0.53 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
--- |
0.80/1.10 |
0.15分钟。 |
| 8615 |
0.13/0.18 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8617 |
0.15/0.20 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8620 |
0.18/0.23 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8622 |
0.20/0.25 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8625 |
0.23/0.28 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8627 |
0.25/0.30 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8630 |
0.28/0.33 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8637 |
0.35/0.40 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8640 |
0.38/0.43 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8642 |
0.40/0.45 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8645 |
0.43/0.48 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8655 |
0.51/0.59 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.15/0.25 |
| 8720 |
0.18/0.23 |
0.70/0.90 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.20/0.30 |
| 8740 |
0.38/0.43 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.20/0.30 |
| 8822 |
0.20/0.25 |
0.75/1.00 |
0.035 |
0.040 |
0.20/0.35 |
0.40/0.70 |
0.40/0.60 |
0.30/0.40 |
| 9254 |
0.51/0.59 |
0.60/0.80 |
0.035 |
0.040 |
1.20/1.60 |
0.60/0.80 |
--- |
--- |
| 9255 |
0.51/0.59 |
0.70/0.95 |
0.035 |
0.040 |
1.80/2.20 |
--- |
--- |
--- |
| 9260 |
0.56/0.64 |
0.75/1.00 |
0.035 |
0.040 |
1.80/2.20 |
--- |
--- |
--- |
注1。上面表中前缀为E的等级通常只通过基本电炉工艺生产。所有其他的通常都是由基本的平炉或基本的氧气工艺生产，但也可以通过调整磷和硫的基本电炉工艺生产。 注2。每道工序的磷和硫限值如下:
|
最大/ % |
|
P |
年代 |
| 基本的电 |
0.025 |
0.025 |
基本平炉
或基本氧 |
0.035 |
0.040 |
| 酸电 |
0.050 |
0.050 |
| 酸性平炉 |
0.050 |
0.050 |
注3。酸性平炉或酸性电炉合金钢的最低硅限值为0.15%。 注4。合金钢中含有少量的某些元素，而这些元素并不是规定或要求的。这些元素被认为是偶然的，可能出现以下最大数量:铜, 0.35%;镍,0.25%;铬0.20%，钼0.06%。 注5。含硫量最低和最高的地方显示的是结果化钢。 注6。上面所示的化学范围和限度是为了检查分析而产生的公差如AISI手册所示。 注7。标准合金钢的铅量程为0.15/ 0.35%。铅只被报道为一个范围，因为它被添加到钢包流在钢被倾倒。 1008|1010|1015|1018|1020|1025|1035|1040|1045|1050|188体育投注地址金博宝1117|1141|1144|12 l14|1215|4140|4150|4340|8620|A36|A653|A513|机械性能|物理性质|碳素钢管标准|工作压力|ASTM A106 B压力温度等级|碳钢|合金钢名称 灰铁正常材料对照表